Irradiation-induced sensitization and stress corrosion cracking of Type 304 stainless steel core-internal components

摘要

High- and commercial-purity heats of Type 304 stainless steel, obtained from neutron absorber tubes after irradiation to fluence levels of up to 2 (times) 10(sup 21) n(center dot)cm(sup (minus)2) (E > 1 MeV) in two boiling water reactors, were examined by Auger electron spectroscopy to characterize irradiation-induced grain- boundary segregation and depletion of alloying and impurity elements. Segregation of Si, P, Ni, and an unidentified element or compound that gives rise to an Auger energy peak at 59 eV was observed in the commercial-purity heat. Such segregation was negligible in high-purity material, except for Ni. No evidence of S segregation was observed in either material. Cr depletion was more pronounced in the high-purity material than in the commercial-purity material. These observations suggest a synergism between the significant level of impurities and Cr depletion in the commercial-purity heat. In the absence of such synergism, Cr depletion appears more pronounced in the high-purity heat. Initial results of constant-extension-rate tests conducted on the two heats in air an in simulated BWR water were correlated with the results from analysis by Auger electron spectroscopy. 15 refs., 10 figs.