Modelling of the Evolution of Stress Corrosion Cracks from Corrosion Pits

A. Turnbull; L.N. McCartney; S. Zhou

首页> 外文期刊>Scripta materialia >Modelling of the Evolution of Stress Corrosion Cracks from Corrosion Pits

【24h】

Modelling of the Evolution of Stress Corrosion Cracks from Corrosion Pits

机译：腐蚀坑中应力腐蚀裂纹演变的建模

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

A mathematical model has been applied to simulate the evolution of stress corrosion cracks from corrosion pits in the short and long crack domains. The distribution of crack-depths in the short crack domain was well represented and some unique features of pit and crack profiles reproduced.

机译：数学模型已被应用来模拟应力腐蚀裂纹在短裂纹区域和长裂纹区域中从腐蚀坑的演变。可以很好地表示出短裂纹域中裂纹深度的分布，并再现了凹坑和裂纹轮廓的一些独特特征。

著录项

来源
《Scripta materialia》 |2006年第4期|共4页
作者
A. Turnbull; L.N. McCartney; S. Zhou;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类金属学与热处理;
关键词
Stress corrosion cracking; Pitting; Modelling;

机译：应力腐蚀开裂;点蚀;建模;
入库时间 2022-08-18 14:37:25

相似文献

外文文献
中文文献
专利

1. Modelling of the Evolution of Stress Corrosion Cracks from Corrosion Pits [J] . A. Turnbull, L.N. McCartney, S. Zhou Scripta materialia . 2006,第4期

机译：腐蚀坑中应力腐蚀裂纹演变的建模
2. Challenges in modelling the evolution of stress corrosion cracks from pits [J] . A. Turnbull, DA Horner, B.J. Connolly Engineering Fracture Mechanics . 2009,第5期

机译：坑应力腐蚀裂纹演化建模的挑战
3. Modelling on the Evolution of Corrosion Pit During Stress Corrosion [J] . LI Junquan Advances in Petroleum Exploration and Development . 2016,第2期

机译：应力腐蚀过程中腐蚀坑的演变建模
4. NEW PERSPECTIVES ON THE EVOLUTION OF STRESS CORROSION CRACKS FROM CORROSION PITS [C] . A. Turnbull, D. A. Homer, B. J. Connolly International Conference on Corrosion and Material Protection . 2007

机译：腐蚀坑应力腐蚀裂缝演变的新观点
5. The coupled environment models for localized corrosions; Crevice corrosion and stress corrosion cracking. [D] . Lee, Sang-Kwon. 2013

机译：局部腐蚀的耦合环境模型；缝隙腐蚀和应力腐蚀开裂。
6. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对X70管线钢在近中性pH环境下点蚀和应力腐蚀开裂行为的综合影响
7. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对近中性pH环境中X70管道钢蚀腐蚀和应力腐蚀开裂行为的综合作用
8. Stress corrosion cracking of titanium alloys - Potential transients at open circuit during SCC and pitting corrosion, and chloride absorption during formation of TiO sub 2 Quarterly progress report, Jul. 1 - 30 Sep. 1967 [R] . Beck, T. R. 1967

机译：钛合金的应力腐蚀开裂 - sCC期间开路时的电位瞬变和点蚀，以及TiO 2形成过程中的氯化物吸收季度进展报告，1967年7月1日至30日

Modelling of the Evolution of Stress Corrosion Cracks from Corrosion Pits

摘要

著录项

相似文献

相关主题

期刊订阅