Ultra-fast densification of boron carbide ceramics under high heating rate and high pressure

摘要

Boron carbide ceramics were obtained in 2 min by a method based on self-propagating high-temperature synthesis plus quick pressing (SHS/ QP). The samples were densified to 98% of theoretical density under a large mechanical pressure (120 MPa) and a fast heating rate (2300 °C/min). The microstructure and mechanical properties were studied. The sample obtained at this heating rate presents an average grain size of 3 μm and a hardness of 34 ± 0.2 GPa.