OXIDATION BEHAVIOR AND ELECTROCHEMICAL CORROSION PERFORMANCE OF Ti_3Al ALLOY WITH TiAl COATING

摘要

Magnetron-sputter deposition was used to produce a Ti–48Al–8Cr–2Ag (at. %) coating on a Ti–24Al–17Nb–0.5Mo (at. %) alloy substrate. Oxidation behavior was studied in air at 900–1000℃. The results indicated that the oxidation rate of sputtered Ti–48Al–8Cr–2Ag nanocrystalline coating was lower than that of the Ti_3Al alloy at 900℃. The former formed a scale of merely Al_2O_3, and the latter formed a scale of TiO_2. However, the Ti–48Al–8Cr–2Ag nanocrystalline coating showed a little bit higher oxidation rate than Ti_3Al alloy at 1000℃ because the outer TiO_2 scale formed and columnar boundaries of the coating gave a larger actual oxidation area than the original alloy. The electrochemical corrosion behavior was investigated in a 3.5% NaCl solution at room temperature. The coating showed excellent electrochemical corrosion resistance in 3.5% NaCl solution because it exhibited stable passive polarization behavior without any overpassivation phenomena.