Fatigue of Cold-Work Tool Steels: Effect of Heat Treatment and Carbide Morphology on Fatigue Crack Formation, Life, and Fracture Surface Observations

摘要

The fatigue properties of two types of cold-work tool steels tempered at various temperatures were evaluated. The microstructure and fracture surface morphology were correlated to the fatigue behavior. Cold-work tool steels using this study were a conventional tool steel (JIS SKD11; 1.4C-11Cr-0.8Mo-0.2V) and its modified steel (M-SKD11; 0.8C-8Cr-2Mo-0.5V). The fatigue strength of the M-SKD11 steel increased 20 pct over that of the SKD11 steel for any number of cycles. This is attributed to the refinement of primary M_7C_3 carbides. These M_7C_3 carbides fractured during fatigue and were found at the sites of fatigue crack initiation. Change in crack initiation behavior was confirmed by acoustic emission testing. The S-N curves of the steels are similar to those of most structural steels. However, the subsurface fatigue crack initiation was dominant at lower alternating stresses. This study points to a general approach of carbide refinement that can be used for the enhancement of fatigue properties.