EBSD analysis of magnesium addition on inclusion formation in SS400 structural steel

摘要

In this study, the effect of magnesium addition on the inclusion formation in SS400 steel was investigated. The experimental specimens with and without Mg addition treatment were compared. The microstructure was observed using optical microscopy after etching with 3% nital. The morphology and chemical composition of the inclusions were analyzed via scanning electron microscopy and energy dispersive spectrometry. The lattice structure and orientation of the inclusions were identified by electron backscattering diffraction. The average size of inclusions in SS400 was between 0.67 and 0.75 μm, and between 0.65 and 0.68 nm in SS400 + Mg. The 2 ppm Mg addition resulted in the oxide formation change from Al_2O_3 to MgOAl_2O_3 and in the inclusion formation change from Al_2O_3-MnS to MgO-Al_2O_3-MnS. Moreover, a simple-phase MnS with an average grain size of 1 μm to 2 μm was observed in rod-like, globular, and polyhedron forms.