Surface analytical and electrochemical study on the role of adsorbed chloride ions in corrosion of stainless steels

摘要

The pitting potential E{sub}(pit) of 18/8 CrNi stainless steels with different sulfur content (0.003, 0.017 and 0.29%) has been determined from potentiodynamic polarization curves in deaerated neutral solutions (0.1 M NaCl and 1 M Na{sub}2SO{sub}4+0.1 M NaCl) with nominally identical chloride content. decreased with increasing sulfur content of the alloy and was about 0.2 V more negative in pure 0.1 M NaCI solution. The chemical composition of the passive film and the adsorbed chloride content have been determined by XPS surface analysis on mechanically polished samples passivated for one hour at potentials below the pitting potential. XPS results show that the surface films are composed in all cases of mixed iron-chromium oxi-hydroxides with a higher chromium content than the bulk composition. The average passive film composition (ca. 40% chromium oxi-hydroxide) and the film thickness (2.3±0.2 nm) were similar for all 18/8 CrNi steels regardless the different sulfur content. The amount of chlorides in the passive film is about twice as high on steels exposed to pure 0.1 N NaCl solution compared to the mixed 1 M Na{sub}2SO{sub}4+0.1 M NaCl solution. Thus the lower pitting potential measured in pure 0.1 N NaCl solution correlates with the higher amount of chloride ions on the passive film surface.