Synthesis of octadecyl acrylate-co-ethylene glycol dimethacrylate resin for removal of dark-colored compound from apple juice and comparison with polyvinylpolypirrolidone (PVPP)

摘要

Adsorption process has an importance for improving the color of juice and also stabilizing the final product during the shelf life. In this study, polyvinylpolypirrolidone (PVPP) and octadecyl acrylate-co-ethylene glycol dimethacrylate (ODA-EGDMA) polymeric resins were used as adsorbents for improving the color properties of apple juice. The ODA-EGDMA resin was prepared by classical suspension polymerization technique and characterized by electron microscopy. The obtained spherical particles diameters were between 20 and 140 mu m. PVPP was selected as reference polymeric material for its importance in the juice industry. The adsorption kinetics of dark-colored compounds on adsorbent polymeric resins were studied at different adsorbent resins concentrations (1, 2, 4, and 8 g adsorbent resin per liter of apple juice) at the constant temperature (20 °C) in batch reactor. Langmuir adsorption model was applied for both PVPP and ODA-EGDMA polymeric adsorbents. The Langmuir isotherms were plotted for both polymeric adsorbents by evaluation of the absorbance data of apple juice at 420 nm. Langmuir isotherm's empirical constants known as K_(ad) and Q_0 were calculated from the equilibrium data. Numerical value of K_(ad) and Q_0 were determined as 5.0578 and 0.3089 for the ODA-EGDMA polymeric resin, 2.4824 and 0.5268 for the PVPP adsorbent, respectively. The scope of this study included comparison of reusability and regeneration properties of the each polymeric adsorbent. For this purpose, series of experiment were done in pack bed column application. Pressure drop measured throughout the PVPP pack bed column was 4.8 times higher than ODA-EGDMA pack bed column at same flow rate (2.5 mL/min) during the this group experiment. ODA-EGDMA resin and PVPP wereregenerated with NaOH (4% w/v, 50 °C) after each run. After regeneration, average removal of dark color (relative absorbance change at 420 nm) of apple juice was determined as 76.47 ± 0.90% for ODA-EGDMA and 91.51 ± 0.86% for PVPP adsorbent resin.