Fabrication of full density near-nanostructured cemented carbides by combination of VC/Cr_3C_2 addition and consolidation by SPS and HIP technologies

摘要

The aim of present work is to study the effect of VC and/or Cr_3C_2 in densification, microstructural development and mechanical behavior of nanocrystalline WC-12wt.%Co powders when they are sintered by spark plasma sintering (SPS) and hot isostatic pressing (HIP). The results were compared to those corresponding to conventional sintering in vacuum. The density, microstructure, X-ray diffraction, hardness and fracture toughness of the sintered materials were evaluated. Materials prepared by SPS exhibits full densification at lower temperature (1100 °C) and a shorter stay time (5 min), allowing the grain growth control. However, the effect of the inhibitors during SPS process is considerably lower than in conventional sintering. Materials prepared by HIP at 1100 °C and 30 min present full densification and a better control of microstructure in the presence of VC. The added amount of VC allows obtaining homogeneous microstructures with an average grain size of 120 nm. The hardness and fracture toughness values obtained were about 2100 HV_(30) and close to 10 MPa m~(1/2), respectively.