Investigation of carbon-carbon composite brake pads in wet and dry sliding wear conditions

摘要

Purpose - The purpose of this study was to investigate wear behaviours of brake pads produced from carbon-carbon (C/C) composites in both wet and dry friction sliding conditions. Carbon is probably the most remarkable element in science and also C/C composites are a family of advanced composite materials. They are the most advanced form of carbon and consist of fibre based on carbon precursors embedded in a carbon matrix. In the present work, wear test specimens were prepared according to the related standards and they were exposed to pin-on-disc wear testing in wet and dry sliding conditions with different loads as 10, 20, 30 and 40 N with 1 m/s constant sliding speed. Wet friction process was conducted on all specimens by means of rain water collected from the nature. Design/methodology/approach - Pin-on-disc wear test tribology lubrication was used. Findings - Mechanical and physical property measurements of C/C composite brake pad materials: hardness, modulus of elasticity, density and water absorption capacity. Wear performance of materials were measured as coefficient of friction, volumetric loss and specific wear rate. Originality/value - C/C composite brake pads are used in railway vehicles. Wear performances of them are very important for safety. In this study, wear behaviours of these materials were investigated not only in dry sliding friction condition but also in wet sliding one. Because safety braking is important in all weather conditions for trains, and we used natural rain water to observe the wet sliding friction behaviour of brake pads. "Water lubrication" is an important aspect mentioned in tribology handbooks.