In vitro study of 24-hour and 30-day shear bond strengths of three resin-glass ionomer cements used to bond orthodontic brackets.

摘要

Interest in using composite resin-glass ionomer hybrid cements as orthodontic bracket adhesives has grown because of their potential for fluoride release. The purpose of this pilot study was to compare shear bond strengths of three resin-glass ionomer cements (Advance, Fuji Duet, Fuji Ortho LC) used as bracket adhesives with a composite resin 24 hours and 30 days after bonding. The amount of adhesive remaining on the debonded enamel surface was scored for each adhesive. Mesh-backed stainless-steel brackets were bonded to 100 extracted human premolars, which were stored in artificial saliva at 37 degrees C until being tested to failure in a testing machine. The hybrid cements, with one exception, had bond strengths similar to those of the composite resin at 24 hours and 30 days. Fuji Ortho LC had significantly lower bond strengths (ANOVA p < or = 0.05) than the other adhesives at 24 hours and 30 days when it was bonded to unetched, water-moistened enamel. Adhesive-remnant scores were similar for all cements, except for cement Fuji Ortho LC when it was bonded to unetched enamel. The resin-glass ionomer cements we tested appear to have bond strengths suitable for routine use as orthodontic bracket-bonding adhesives.