Effect of oxygen content on thermal conductivity of sintered silicon nitride

摘要

Silicon nitride powders with concurrent addition of Yb_2O_3 and MgO were sintered at 1900 deg C for 2-48 h under 0.9 MPa nitrogen pressure. Microstructure, lattice oxygen content and thermal conductiity of the sintered specimens were evaluated. All specimens had a duplex microstructure composed of small matrix grains and elongated grains. Thermal conductivities of sintered bodies were remarkably increased with sintering time and reached a maximum value of about 120 W(centre dot)m~(-1)(centre dot)K~(-1). The lattice oxygen content of dense silicon nitride sintered body decreased with sintering time. The thermal conductivity increased with decreasing the lattice oxygen content. So far, it was reported that the thermal conductivity of Si_3N_4 was affected by grain size and morphology, composition and thickness of grain boundary layer. It was revealed that thermal conductivity of sintered specimen was closely related to the oxygen content present in the silicon nitride lattice.