Viscoplastic crack initiation and propagation in crosslinked UHMWPE from clinically relevant notches up to 0.5 mm radius

摘要

Highly crosslinked UHMWPE is now the material of choice for hard-on-soft bearing couples in total joint replacements. However, the fracture resistance of the polymer remains a design concern for increased longevity of the components in vivo. Fracture research utilizing the traditional linear elastic fracture mechanics (LEFM) or elastic plastic fracture mechanics (EPFM) approach has not yielded a definite failure criterion for UHMWPE. Therefore, an advanced viscous fracture model has been applied to various notched compact tension specimen geometries to estimate the fracture resistance of the polymer. Two generic crosslinked UHMWPE formulations (remelted 65 kGy and remelted 100 kGy) were analyzed in this study using notched test specimens with three different notch radii under static loading conditions. The results suggest that the viscous fracture model can be applied to crosslinked UHMWPE and a single value of critical energy governs crack initiation and propagation in the material. To our knowledge, this is one of the first studies to implement a mechanistic approach to study crack initiation and propagation in UHMWPE for a range of clinically relevant stress-concentration geometries. It is believed that a combination of structural analysis of components and material parameter quantification is a path to effective failure prediction in UHMWPE total joint replacement components, though additional testing is needed to verify the rigor of this approach.