Cyclic fatigue of silica refractories – effect of test method on failure process

摘要

Silica refractories serving in high temperature industrial installations fail due to thermo-mechanical cyclic loads. The failure process was investigated by performing cyclic fatigue tests of several methods. In uni-axial compression the samples were tested either with constant force or displacement amplitude or with fixed upper displacement limit. In bending constant displacement amplitude tests were done. The investigation was supported by monotonic loading tests and microstructural analysis. It was deter-mined that the fatigue failure occurs due to the degradation of interlocking in the crack wake. Cracking of larger grains is important for the crack initiation. The test set-up and the loading procedures signifi-cantly influence the potential to resist the crack propagation. Cyclic loading produces less brittle failure than monotonic loading. The displacement controlled method allows more gradual, less brittle, failure than the force controlled method. The potential of the crack arrest is less developed in bending than in compression.