Influence of the heating rate on grain size of alumina ceramics prepared via spark plasma sintering (SPS)

摘要

The dependence of grain size on the heating rate has been investigated for alumina ceramics prepared via spark plasma sintering (SPS). For this purpose, the local grain size has been determined via position-dependent microscopic image analysis, using two independent grain size measures (mean chord length and Jeffries grain size). For alumina ceramics prepared with heating rates between 5 and 100 degrees C/min (pressure 80 MPa, maximum temperature 1300 degrees C) it is found that for higher heating rates the grain size is smaller. However, the microstructural non-uniformity is so large that any grain size determination that does not take this non-uniformity into account becomes meaningless, because grain size gradients from the specimen periphery to the center are larger than the differences in grain size due to different heating rates. Temperature and pressure gradients are discussed as the most plausible reasons for the microstructural non-uniformity.