Hybrid organic-inorganic materials on the basis of acrylic monomers and TEOS prepared by simultaneous UV-curing and sol-gel process

摘要

In this work cross-linked hybrid organic-inorganic membranes consisting of polymeric matrix functionalized with sulfonic groups and uniformly distributed silica domains have been successfully synthesized through in situ polymerization strategy via photo-initiated copolymerization of acrylic monomers (acrylonitrile AN, acrylamide AAm, 3-sulfopropyl acrylate potassium salt SPAK) and simultaneous formation of silica counterpart using TEOS-based sol-gel system. N,N'-methylenebis(acrylamide) (MBA) was used as a cross-linker. The ratio between monomers was maintained stable, whereas the amount of added sol-gel system was varied. The influence of inorganic component content on properties of hybrid polymer-inorganic membranes was investigated. Chemical composition, thermal properties, structure and morphology of the obtained hybrid membranes were investigated by ATR-FTIR, TGA, DSC, SEM and EFTEM. Proton conductivity of the synthesized membranes was high (7.6 to 13.5 mS/cm) and increases with an increase of silica content. The prepared membranes were thermally stable up to 90 degrees C, and exhibited proton conductivity and swelling coefficients sufficient for possible use as proton-conducting membranes.