The Effect of Heat Treatment Process Parameters on Mechanical Properties, Precipitation, Fatigue Life, and Fracture Mode of an Austenitic Mn Hadfield Steel

摘要

In this study, the effect of cooling rate after heat treatment on mechanical properties, fatigue life, precipitation and fracture mode of an austenitic Mn Hadfield steel was investigated. Cast samples of the Hadfield steel were heat treated at 1100??C for 2?h. The samples were subsequently quenched in pure water and also in 3?wt.% NaCl salt bath. Optical microscope (OM) and scanning electron microscope (SEM) were used to analyze microstructure and?fracture surfaces. Transmission electron microscope (TEM) was used to assess the precipitates. X-ray diffraction (XRD) was used to determine the phases formed. Mechanical properties and fatigue life were determined by uniaxial tensile test, bending fatigue and hardness measurements. Results showed that the sample quenched in salt bath had lower Mn~(3)C precipitates, hardness, yield and tensile strengths. Instead, this situation resulted in a more ductile fracture mode and higher formability. Finally, the fatigue life of the sample quenched in salt bath was longer than the one quenched in pure water.