Microstructure and Mechanical Properties of MoSi2 Coating Deposited on Mo Substrate by Hot Dipping Processes

摘要

MoSi2 coating was deposited on Mo substrate by a hot dipping process within the silicon bath. The effects of the hot dipping temperature and time on the thickness and mechanical properties of MoSi2 coating have been investigated. The results indicated that the average hardness of MoSi2 coating is only 209.15 MPa, and the average flexural strength is 873.63 MPa. Therefore, the MoSi2 coating deposited on Mo substrate exhibit better mechanical properties than monolithic MoSi2 and MoSi2-based composites. In addition, the hot dipping processes have an important influence on mechanical properties. The hardness and flexural strength decrease sharply with increasing hot dipping temperature, then increases slightly on increasing hot dipping temperature. Meanwhile, the hardness and flexural strength increase sharply with increasing hot-dipping time.