y (Fe x Ni 1- x ) 4Sb 12 ( x?=?0.45, 0.50, 0.70, 1) thermoelectric compounds]]>

摘要

Skutterudites are interesting compounds for thermoelectric applications. The main drawback in the synthesis of skutterudites by solidification of the melt is the occurrence of two peritectic reactions requiring long annealing times to form a single phase. Aim of this work is to investigate an alternative route for synthesis, based on rapid solidification by planar flow casting. The effect of cooling rate on phases formation and composition, as well as on structure, microstructure and mechanical properties of the filled Smy(FexNi1-x)4Sb12(x?=?0.45, 0.50, 0.70, 1) skutterudites was studied. Conversely to slowly cooled ingots, rapidly quenched ribbons show skutterudite as the main phase, suggesting that deep undercooling of the liquid prevents the nucleation of high temperature phases, such as (Fe,Ni)Sb and (Fe,Ni)Sb2. In as-quenched samples, a slightly out of equilibrium Sm content is revealed, which does not alter the position of thep/nboundary; nevertheless, it exerts an influence on crystallographic properties, such as the cell parameter and the shape of the Sb4rings in the structure. As-quenched ribbons show a fine microstructure of the skutterudite phase (grain size of 2–20?μm), which only moderately coarsens after annealing at 873?K for 4 days. Vickers microhardness values (350–400 HV) of the skutterudite phase in as-quenched ribbons are affected by the presence of softer phases (i.e.Sb), which are homogeneously and finely dispersed within the sample. The skutterudite hardens after annealing as a consequence of a moderate grain growth, which limits the matrix effect due to the presence of additional phases.