Evaluation of corrosion resistance of Co-Cr alloys fabricated with different metal laser sintering systems

摘要

PURPOSE. The aim of this study was to evaluate the corrosion resistance of the specimens produced by five different commercial metal laser sintering (MLS) systems with their recommended Co-Cr alloy powders. MATERIALS AND METHODS. The MLS machines and the alloy powders used were, ProX 100-ST2724G (St-Pro), Mysint 100-EOS SP2 (SP2-Mys), EOSINT 270-EOS SP2 (SP2-EOS), SLM 100-Starbond CoS (SB-SLM), and MLab Cusing-Remanium (R) Star (RS-MLab), respectively. Eight specimens from each group were prepared. Open circuit potential (E-ocp) and electrochemical impedance spectroscopy (EIS) measurements of polished surfaces of the specimens were conducted in a three-electrode cell using a potentiostat-galvanostat in Fusayama-Meyer artificial saliva (AS). Specimens from each group were immersed in AS and de-ionized water for seven days. E-ocp, charge transfer resistance (R-alpha) values, and released ions (mu g/cm(2) x 7d) in different solutions were determined. The specimen surfaces were observed with SEM/EDS. Results were analyzed statistically. RESULTS. E-ocp values have shifted to potentials that are more positive over time. Steady-state E-ocp values were from high to low as follows, SB-SLM, SP2-Mys, SP2-EOS, RS-MLab, and ST-Pro, respectively. After 60 mins, RS-MLab specimens had the highest R-alpha value, followed by SP2-Mys, SB-SLM, SP2-EOS, and ST-Pro. In all groups, ion release was higher in AS than that in de-ionized water. CONCLUSION. There were small differences among the corrosion resistances of the Co-Cr alloy specimens produced with MLS systems; meanwhile, the corrosion resistances were quite high for all specimens.