Dislocation loop evolution in F/M steel T91 under in-situ ion irradiation: Influence of the presence of initial dislocations

摘要

Ferritic/Martensitic (F/M) steel T91 was irradiated in-situ to 4 and 10 dpa at 470 degrees C using 1 MeV Kr2+. The microstructure evolution under irradiation was followed and characterized by in-situ Transmission Electron Microscopy (TEM), in terms of dislocation loop Burgers vector, average size and density as a function of dose. Furthermore, the influence of the presence of dislocations in the pre-irradiated matrix was investigated by comparing the radiation induced defect evolution in grains with and without initial dislocations. (C) 2020 Elsevier B.V. All rights reserved.