Dielectric and ferroelectric properties of SrTiO3-Bi0.54Na0.46TiO3-BaTiO3 lead-free ceramics for high energy storage applications

摘要

The need of lead-free ceramics with excellent dielectric behaviors and high energy storage properties have been extensively studied. In this study, (1-x)SrTiO3-x(0.94Bi(0.54)Na(0.46)TiO(3)-0.06BaTiO(3)) ((1-x)ST-xBNBT) lead-free ceramics were designed and fabricated using the conventional solid state sintering method. The results demonstrate that the dielectric constant of (1-x) ST-xBNBT ceramics increases gradually and reaches the maximumvalue (similar to 3940) with x = 0.6 at 100 Hz, which is 11.94 times as large as that of pure SrTiO3 (similar to 330), and the dielectric loss is lower than 0.20 at the measured frequencies for all the samples. Meanwhile, the dielectric measurements reveal an intensified diffusion and relaxor behavior. All the samples show slim polarization-electric field (P-E) loops, and the optimal recoverable energy storage density (W-rec) of 1.88 J/cm(3) together with high energy storage efficiency (eta) of 79% can be achieved with x = 0.5, which indicates that the (1-x)ST-xBNBT ceramics may be promising lead-free ceramics for high energy storage applications. (C) 2018 Elsevier B.V. All rights reserved.