Effect of CuO/MnO additives on microstructure and microwave dielectric properties of 3ZrO(2)-3TiO(2)-ZnNb2O6 ceramics

摘要

The effect of CuO/MnO additives on phase composition, microstructures, sintering behavior, and microwave dielectric properties of 3ZrO(2)-3TiO(2)-ZnNb2O6 (3Z-3T-ZN) ceramics prepared by conventional solid-state route were systematically investigated. CuO/MnO doped ceramics exhibited a main phase of alpha-PbO2-structured ZrTi2O6 and a secondary phase of rutile TiO2. SEM results showed that the grain size of MnO doped ceramics became larger with increasing amount of dopants. The presence of CuO/MnO additives effectively reduced the sintering temperature of 3Z-3T-ZN ceramics to 1220 degrees C. MnO doped into ceramics could enhance the Q x f values significantly. The 0.5 wt% CuO doped 3Z-3T-ZN ceramics with 0.5 wt% of MnO, sintered at 1220 degrees C for 4 h, was measured to show superior microwave dielectric properties, with an epsilon(r) of 41.02, a Q x f value of 44,230 GHz (at 5.2 GHz), and tau(f) value of +2.32 ppm/degrees C. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.