Research of Deformation and Fracture of Annealed Metallic Glass in High Temperature Area under the Local Loading

摘要

Regularities of crack formation of metallic glass 82K3XCP, annealed at high temperatures, after microindentation on different substrates were investigated. The linear dependencies of crack formation probability from the indenter load were established. It was shown that application of elastic substrate is preferable in determining mechanical characteristics of metallic glass.