Influence of countersurface materials on dry sliding performance of CuO/Y-TZP composite at 600 °C

摘要

Dry sliding wear tests on 5 wt.% copper oxide doped yttria stabiUzed zirconia poly crystals (CuO-TZP) composite have been performed against alumina, zirconia and silicon nitride countersurfaces at 600 °C. The influences of load and countersurface materials on the tribological performance of this composite have been studied. The friction and wear test results indicate a low coefficient of friction and specific wear rate for alumina and zirconia countersurfaces at F= 1N load (maximum Hertzian pressure ~0.5 GPa). Examination of the worn surfaces using scanning electron microscope/energy dispersive spectroscopy confirmed the presence of copper rich layer at the edge of wear scar on the alumina and zirconia countersurfaces. However, Si_3N_4 countersurface sliding against CuO-TZP shows a relatively higher coefficient of friction and higher wear at 1N load condition. These results suggest that the countersurface material significantly affect the behavior of the third body and self-lubricating ability of the composite.