The inhibition mechanism of pitting corrosion of pure aluminum by nitrate and sulfate ions in neutral chloride solution

摘要

The inhibition mechanism of pitting corrosion of natural oxide film-covered pure aluminum by NO~-_3 and SO~(2-)_4 ions has been examined in 0.1 M NaCl solution using potentiodynamic polarization experiments, a.c.impedance spectroscopy, Auger electron spectroscopy and a combination of the potentiostatic current transient method and optical microscopy. It was found that NO~-_3 ions can be incorporated into the natural oxide film on pure aluminum at open-circuit potential, but the incorporation of SO~(2-)_4 ions into the film hardly occurs. The incorporation of NO~-_3 ions lowered the pitting susceptibility of pure aluminum in 0.1 M NaCl solution. Based upon the experimental results, it is suggested that the pitting corrosion inhibition mechanism by anions can be classified into two different groups: inhibition by competitive adsorption of anions (SO~(2-)_4) with Cl~- ions and inhibition by the incorporation of anions (NO~-_3) into the film rather than competitive adsorption. Both cases may impede the incorporation of Cl~- ions into the film, thus inhibiting pitting corrosion of natural oxide film-covered pure aluminum in chloride solutions.