Effects of Temperature and Blank Holding Force on Biaxial Forming Behavior of Aluminum Sheet Alloys

摘要

Biaxial forming behavior is investigated for three aluminum sheet alloys (Al 5182 containing 1 percent Mn (5182 + Mn), Al 5754, and 6111-T4) using a heated die and punch in the warm forming temperature range of 200-350 deg C, It is found that, while all three alloys exhibit significant improvement in their formability compared with that at room temperature, the non-heat-treatable alloys 5182 + Mn and 5754 give higher part depths than that of heat-treatable 6111-T4. The formability generally increases with decreasing BHP (BHP), but increasing the forming temperature and/or BHP minimizes the wrinkling tendency and improves the forming performance. The stretchability of the sheet alloys increase with increasing temperature and increasing BHP. For the alloys and forming conditions involved in the current study, the form-ability, measured in terms of part depth, comes mainly from the drawing of metal into the die cavity, although stretching effects do influence the overall forming behavior. The optimum formability is achieved by setting the die temperature 50 deg C higher than the punch temperature to enhance the drawing component. Setting the die temperature higher than the punch temperature also improves the strain distribution in a part in such a manner that postpones necking and fracture by altering the location of greatest thinning.