Effect of Semi-Solid Processing on Iron-bearing Intermetallic Compounds in A380 Aluminum Alloy

摘要

AI-Si-Cu alloys are a general purpose of die casting alloys, widely used to manufacture automotive parts by forming processes to modify their properties. In the present work, low superheat melt was employed to produce modified microstructure and non-dendritic A3 80 alloy feed stocks. The melt was cast on a cooling slope plate at 615 ℃ to, obtain ingots. Then, ingots are thixoformed using a hydraulic press after heating them at 570 ℃ for, 15 minutes, yielding a microstructure with predominantly a-Al globules,Si particles, and modified β-phase intermetallic compounds. The effect of semi-solid processing on the morphology, size, and distribution of iron-bearing intermetallics was studied. The results or image analysis of the samples showed that by using semi-solid method, the shape factor of a-AI phase improved, and iron containing intermetallics were modified in size and distribution. These changes in the aspect ratio and redistribution of the intermetallics improved the mechanical properties such as hardness of the products.