Comparison between a novel nickel-titanium alloy and 508 nitinol on the cyclic fatigue life of ProFile 25/.04 rotary instruments.

摘要

ProFile 25/.04 instruments manufactured from three variants of Nitinol (1A, 1B & 2AS) were compared with stock production ProFile 25/.04 instruments and fatigue tested to failure. Cyclic fatigue testing was performed by rotating instruments at 300 RPM in a simulated steel root canal with 5 mm radius and 90 degrees curve until instrument separation. Time to failure was recorded. Torsion testing was undertaken by clamping 3 mm of each instrument tip between brass plates and rotating it at 2 RPM until failure. Data were recorded for torque and angle at fracture. Statistical differences were found with nickel-titanium variant 1B (M-Wire NiTi) nearly 400% more resistant to cyclic fatigue than stock ProFile 25/.04 (P < .001). Torsion testing found differences between all 508 Nitinol groups and M-Wire NiTi (P < .001). ProFile 25/.04 files manufactured from M-Wire NiTi have significantly greater resistance to cyclic fatigue while maintaining comparable torsional properties.