Low Temperature Sintered Ni-Zn-Cu Ferrite

摘要

The low temperature sintering of Ni-Zn-Cu ferrite lias been investigated by usual ceramic technique. The sintering density and the permeability of the sintered ferrite were strongly affected by the size of the starting oxide powders and the pre-sintering temperature. It was most effective to utilize line particles of iron oxide and to calcine at about HO(I::C for the preparation of high permeability ferrite. The sintered ferrite with a density greater than 4.5g/cc and the permeability at 10MHz greater than 200 was obtained at relative low sintering temperature.(about 900°C). This condition is suitable for multilayer chip inductor application.