Effect of ultrasonic cavitation erosion on corrosion behavior of high-velocity oxygen-fuel (HVOF) sprayed near-nanostructured WC-10Co-4Cr coating

摘要

The effect of ultrasonic cavitation erosion on electrochemical corrosion behavior of high-velocity oxygen-fuel (HVOF) sprayed near-nanostructured WC-10Co-4Cr coating in 3.5 wt.% NaCl solution, was investigated using free corrosion potential, potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) in comparison with stainless steel 1Cr18Ni9Ti. The results showed that cavitation erosion strongly enhanced the cathodic current density, shifted the free corrosion potential in the anodic direction, and reduced the magnitude of impedance of the coating. The impedance of the coating decreased more slowly under cavitation conditions than that of the stainless steel 1Cr18Ni9Ti, suggesting that corrosion behavior of the coating was less affected by cavitation erosion than that of the stainless steel. (C) 2015 Elsevier B.V. All rights reserved.