A closer look: Magnetic behavior of a three-dimensional cyanometalate coordination polymer dominated by a trace amount of nanoparticle impurity

摘要

The structure and properties of the K{Ni[Au(CN)(2)](3)} coordination polymer, prepared as a powder at room temperature and recrystallized livch-othernially, are reported. The structure of K{Ni[Au(CN)(2)](3)} contains triply-interpenetrated Prussian Blue type pseudo-cubic arrays assembled from the alternation of octahedral Ni-11 centers and [Au(CN)(2)](-) bridging units. SQUID magnetometry studies have shown that K{Ni[Au(CN)(2)](3)} displays typical paramagnetic behavior for isolated Ni-11 centers clown to 1.8 K. However, the magnetic behavior of the samples prepared under hydrothermal conditions suggests a superparamagnetic signature superimposed onto a paramagnetic background. After investigating the samples by transmission electron microscopy, it was determined that, in addition to K{Ni[Au(CN)(2)](3)}, the high-temperature (125, 135, and 165 degrees C) aqueous reaction of Ni(NO3)(2)center dot 6H(2)O with KAu(CN)(2) also led to the formation of nanoparticles of NiO and Au as minor side products, and that these dominated the magnetic behavior. Nanoparticles of various sizes and shapes were observed, depending on the reaction conditions. Samples containing nanoparticles were found to be superparamagnetic, exhibiting blocking temperatures of approximate to 17-22 K, consistent with the behavior expected for NiO nanoparticles. These results illustrate the extreme care that must be taken when examining the physical properties of apparently analytically pure materials prepared by hydrothermal methods.