Study of the anticorrosive behaviour of epoxy binders containing non-toxic inorganic corrosion inhibitor pigments

摘要

The anticorrosive performance of epoxy coatings pigmented with non-toxic corrosion inhibitors pigments was investigated in this work. The coatings used contained the following pigments: zinc phosphate (ZP), zinc phosphomolybdate (ZPM) and zinc calcium phosphomolybdate (ZCPM). For comparative studies epoxy coatings with the following compositions were made up: one only with filler (CRG); one without pigments, varnish (VR) and other with zinc chromate (ZC) pigment. The corrosion inhibitor performance of the coatings was evaluated by immersion tests in 0.01 mol L-1 NaCl aqueous solutions and accelerated tests in a salt spray chamber. The corrosion inhibitor performance of the samples was monitored using open-circuit potential (E-oc) measurements and electrochemical impedance spectroscopy (EIS) technique. Complementary tests were carried out using water vapour permeability of free-standing films and thermogravimetric (TG) analysis. The permeability test showed that the addition of the studied pigments did not modify the barrier properties of the free-films in comparison that pigmented with chromate. Thermal analysis indicated that the addition of the pigments improved the thermal stability of the coatings and it suggested a resin/pigment interaction. The total immersion tests and salt spray tests demonstrated that the barrier properties of the coatings pigmented with the inhibitors were not degrading as much as that pigmented with ZC. Therefore, all the three pigments could replace ZC as an anticorrosive pigment in similar conditions to those described here. The best corrosion inhibitor performance in the total immersion test was presented by the ZPM and ZCPM coatings while in the salt spray test the corrosion inhibitor performance of all the three pigmented coatings was similar, suggesting that only in the less aggressive test is possible to detect any difference between the coatings with the non-toxic pigments. (C) 2008 Elsevier B.V. All rights reserved.