Influence of curing conditions on the mechanical and physical properties of chemically-activated phosphorous slag cement

摘要

In this paper, the influence of curing time and temperature on the compressive strength development of chemically-activated high phosphorous slag content cement composed of phosphorous slag (80 wt.%), Portland cement (14 wt.%), and a compound chemical activator consisting of sodium sulphate and anhydrite (6 wt.%) is investigated. For this purpose, mortar specimens were prepared and cured in lime-saturated water at different temperatures of 25, 45, 65, 85, and 100 degrees C in an oven and at temperatures of 165 and 200 degrees C in autoclave. Results showed that the ultimate compressive strength decreases at curing temperatures higher than 45 degrees C. Investigations by XRD and FTIR show that curing at temperatures higher than 45 degrees C results in the formation of alpha-C2SH. (C) 2015 Elsevier B.V. All rights reserved.