The Effect of Titania Content on the Refractive Index of Titania/ Polyimide Composite Films Prepared by the Sol-Gel Process SHORT COMMUNICATION

摘要

Titania/polyimide composite films were fabricated from a polyamic acid of pyromellitic dianhydride (PMDA)/4,4'-oxydianiline (ODA) as a polyimide precursor and titanium n-butoxide by the sol-gel process.The ratio of titania weight to the combined weight of polyamic acid and titania,W,was up to 0.4,assuming complete conversion of titanum n-butoxide to titania.Refractive index dispersions and extinction coefficients of the prepared films were measured in the wavelength range from 400 to 800 nm by ellipsometer.Refractive index at a wavelength of 633 nm was increased from 1.67 for a pure polyimide to 1.77 for the titania/polyimide composite film at W=0.4.