強磁場中示差熱分析によるFe-Cのα→γ変態に対する強磁場効果

摘要

The magnetic field effect on the α-γ transformation of hypoeutectoid steels (Fe-0.1wt.%C, Fe-0.23wt.%C, and Fe-0.47wt.%C) were investigated by differential thermal analysis under high magnetic fields B up to 26 T. The magnetic field effects for the transformation temperatures A_1 (α-Fe + Fe3C → α-Fe + γ-Fe) and A_3 (α-Fe + γ-Fe → γ-Fe) were different from each other. The increment of A_1 induced by the magnetic field was independent from the carbon concentration. A_1 increased linearly for the magnetic field for B ＜ 10 T, whereas A_1 increased quadratically for B ＞ 20 T. A_3 for Fe-0.23 wt.%C increased quadratically against B. When the magnetic field of 26 T was applied, A_1 and A_3 for Fe-0.47wt.%C increased 35 K and 53 K， respectively. The magnetic field effects for the A_1 and A_3 are discussed on the basis of the gain of Zeeman energy for α-Fe.%市販の亜共析鋼について強磁場中示差熱分析を行い，α-γ相変態温度に対する強磁場効果を明らかにした。A_1温度は炭素組成によらず磁場に対して増加する。このとき，点がα-Feのキュリー温度より低い20T以下の磁場に対してA_1点は直線的に上昇するが，A_1点がα-Feのキュリー温度付近になる20T以上では磁場の2乗で増加するように振る舞う。一方，α-Feのキュリー温度より十分高いFe-0.23wt.%CのA_3点は磁場に対して近似的に2乗で上昇する。