The effect of a high power ion beam of nanosecond duration on layers of organic polymers - chlorinated polyvinyl chloride, polyvinyl chloride, composition - polyvinyl chloride + polyvinylidene chloride, vinyproz (vinyl chloride and methyl methacrylate copolymer), polyvinyl acetate, polyvinylidene fluoride, polyvinyl alcohol containing catalytic additives of inorganic and organic iron compounds was investigated. The formation of carbon nanofibers with a diameter of 30-150 nm and a length of up to 10 μm on the surface of of chlorine-containing polymers and their compositions under the action of a high power ion beam has been observed. On the surface of the other investigated polymers after the action of high power ion beam the formation of carbon nanofibers has not been established. The possible mechanism of the influence of the nature of the polymer on the formation of nanostructured carbon on the surface of the investigated polymers under the action of a high power ion beam is discussed.%Исследовано воздействие мощного ионного пучка наносекундной длительности на слои органических полимеров: хлорированного поливинилхлорида, поливинилхлорида, композиции поливинил-хлорид + поливинилиденхлорид, винипроза (сополимера винилхлорида и метилметакрилата), по-ливинилацетата, поливинилиденфторида, поливинилового спирта, содержащих каталитические добавки неорганических и органических соединений железа. Обнаружено образование углеродных нановолокон диаметром 30-150 нм и длиной вплоть до 10 мкм на поверхности хлорсодержащих полимеров и их композиций при воздействии мощного ионного пучка. На поверхности остальных исследованных полимеров после воздействия мощного ионного пучка образования углеродных нановолокон не установлено. Обсуждается возможный механизм влияния природы полимера на формирование наноструктурированного углерода на поверхности исследованных полимеров при воздействии мощного ионного пучка.
展开▼