Mixing enthalpy and heat content measurements of liquid binary iron-niobium alloys

摘要

The mixing enthalpy of the system iron-niobium has been determined at 1935 and 2035 K for alloys having _Nb mass contents of up to 51.5 percent by the levitation alloying calorimetry (LAC). Moreover, by means of the combination of an electromagnetic levitation unit with a drop calorimeter the temperature functions of the enthalpies of the eutectic alloys Fe_(89.4)Nb_(10.6) and Fe_(41)Nb_(59) and the congruent melting compound Fe_2 Nb have been measured in the liquid state and below their melting points. From these values the melting enthalpies and entropies are calculated. The experimental results are compared with literature data. In consideration of the standard formation enthalpy of the alloys their enthalpy values could be connected with the mixing enthalpy.%Die Mischungsenthalpie des Systeme Eisen-Niob wurde bei Temperaturen von 1935 und 2035 K ausgehend vom reinen Eisen bis zu Nb Massenanteilen von 51.5 percent mittels Schwebeschmelz-Vereinigungskalorimetrie gemessen und mit Literaturwerten verglichen. Weiterhin wurden unter Ein-satz der elektromagnetischen Schwebeschmelz-Dropkalorimetrie die Temperaturfunktionen der Enthalpien der eutektischen Legierungen Fe_(89.4)Nb_(10.6) und Fe_(41)Nb_(59) sowie der kongruent schmelzenden Verbindung Fe_2Nb im flussigen Zustand und unterhalb ihrer Schmelzpunkte hest:mmt, so dass die Schmelzenthalpien und Entropien berechnet werden konnten. Unter Berucksichtigung der Standardbildungsenthalpie ist es moglich, die Enthalpien der Legierungen mit der Mischungsenthalpie zu verknupfen.