PRELIMINARY REPORT ON SUPESTRUCTURING IN MERCURIAN TETRAHEDRITE FROM GANT, TIROL, AUSTRIA

摘要

Small scale ordering is observed on the electron diffraction and dark-field images of Hg-tetrahedrite. Essentially three types of ordering are observed: 1. large rectangular lamellae with the size of 15 x 120 pro. (type A), 2. thin long needles with the size of 1 x 120 pm located at the edge of lamellae A (type B), 3. two types of oblique multiple lamellae with the size of 1.5 x 20 and 0.5 x 20 pm building up lamellae A (type C). The observed lamellae are probably induced by Sb—As ordering on the M_4~(3+) site, and by Hg~(2+) - Zn~(2+) as well as Hg~(2+)-Cu~(2+) ordering on the M_2~(2+) site in tetrahedrite-tennantite molecule represented by formula M_(10)~+ M_2~(2+) M_4~(3+) S_(13).%Uporządkowanie w małej skali jest obserwowane na elektrogramach dyfrakcyjnych oraz na obrazach w ciemnym polu otrzymanych z tetraedrytu rtęciowego. Zaobserwowano trzy typy uporządkowania: 1. duże prostokątne lamelle o wymiarach 15 x 120 pm (typ A), 2. cienkie wydłużone igły o wymiarach 1 x 120 pm lokujące się na obrzeżach lamelli A (typ B), 3. dwa typy ukośnych, polisyntetycznych lamelli o wymiarach 1,5 x 20 i 0,5 x 20 pm budujące lamelle A (typ C). Obserwowane lamelle są prawdopodobnie wynikiem uporządkowania Sb-As na pozycji M_4~(3+) oraz uporządkowania Hg~(2+)-Zn~(2+) i Hg~(2+)-Cu~(2+) na pozycji M_2~(2+) w tetraedrycie-tennantycie (M_(10)~+ M_2~(2+) M_4~(3+) S_(13)).