Effect of Superficially Applied Y₂O₃ Coating on High-Temperature Corrosion Behavior of Ni-Base Superalloys

摘要

Inhibitors and oxide additives have been investigated with varying success to control high-temperature corrosion. Effect of Y₂O₃ on high-temperature corrosion of Superni 718 and Superni 601 superalloys was investigated in the Na₂SO₄-60 pct V₂O₅ environment at 1173 K (900 °C) for 50 cycles. Y₂O₃ was applied as a coating on the surfaces of the specimens. Superni 601 was found to have better corrosion resistance in comparison with Superni 718 in the Na₂SO₄-60 pct V₂O₅ environment. The Y₂O₃ superficial coating was successful in decreasing the reaction rate for both the superalloys. In the oxide scale of the alloy Superni 601, Y and V were observed to coexist, thereby indicating the formation of a protective YVO₄ phase. There was a distinct presence of a protective Cr₂O₃-rich layer just above the substrate/scale interface in the alloy. Whereas Cr₂O₃ was present with Fe and Ni in the scale of Superni 718. Y₂O₃ seemed to be contributing to better adhesion of the scale, as comparatively lesser spalling was noticed in the presence of Y₂O₃.