Effect of oxidation on the compressive strength of sintered SiC-fiber bonded ceramics

摘要

The compressive strength of SiC-fiber bonded ceramics obtained from hot-pressed amorphous Si-Al-C-O fibers and its degradation by high temperature exposure to an oxidizing environment was studied. Compressive strength was measured at room temperature as a function of strain rate, orientation, and oxidation temperature. Weight loss was monitored as a function of exposure time in atmospheric air at temperatures ranging from 800 to 1600℃, for times ranging from 0.5 to 5 h. Room-temperature compressive strength had a moderate decrease after exposures at 800℃ associated to carbon burnout; increased for exposures in the range 1000-1500℃ due to a defect-blunting action of the silica scale; and decreased significantly at 1600℃ due to extensive surface recession.