Boehmite nanopetals self assembled to form rosette-like nanostructures

摘要

Rosette-like boehmite nanostructures were prepared successfully via a simple hydrothermal process. The obtained material was characterized with X-ray powder diffractometry (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Using Scherrer formula, the average crystallite size of the obtained boehmite rosettes was measured to be about 8 nm. It was shown that boehmite nanopetals with average width of about 41 nm determined by TEM, were formed during the hydrothermal process and then self assembled due to weak hydrogen bonds to fabricate boehmite rosettes. The specific surface area of the obtained rosette-like nanostructures was calculated through BET N_2-adsorption technique to be about 143.08 m~2/g.