Preparation and ring rolling processing of large size Ti-6Al-4V powder compact

摘要

This study reports the feasibility to fabricate large size Ti-6Al-4V alloy parts using the retained powder after screened out the finer powder for additive manufacturing. Effects of powder size on the microstructure and mechanical properties of powder compacts were studied. Effects of HIPing cycle on relative density distribution of large size powder compact were also investigated. Hot compression tests of as-HIPed powder compact were conducted. Prediction of temperature field distribution of large size powder compact during ring rolling was obtained though finite element method (FEM). The results showed that the powder size has no obvious influence on the microstructure and mechanical properties of as-HIPed Ti-6Al-4V alloy. The homogeneous as-HIPed powder compact with large dimensions can be produced through an optimized HIPing schedule. The optimized hot working processing window from the isothermal compression tests is temperature at 940-970 degrees C and strain rate at 1-10s(-1). The hot workability of Ti-6Al-4V powder compact is comparable or better than that of as-cast alloys. On the basis of isothermal compression tests and FEM results, a large workpiece of Ti-6Al-4V powder component has been successfully formed by ring rolling, and the mechanical performance of ring-rolled powder compact have some improvements than that of as-HIPed alloys. (C) 2016 Elsevier Ltd. All rights reserved.