Compatibilization of high density polyethylene/polyisoprene blends with polyethylene/polyisoprene 'thread-through' copolymers

摘要

The compatibilization of high density polyethylene (HDPE)/polyisoprene (PI) blends with polyethylene/polyisoprene (PE/PI) "thread-through" copolymers was investigated. The proliferating structure of PE/PI with segments chemically identical to HDPE and PI, respectively, is different from that of graft copolymers. Studies showed that the dispersed domain size in the blends was significantly reduced and interfacial adhesion was improved by the compatibilization action of the copolymer. In the differential scanning calorimetry (DSC) analysis, the crystallization peak of HDPE in the blends became broad with adding the copolymer and fractionated crystallization appeared in the HDPE/PI blend compatibilized with the copolymer at a weight ratio of 30/70 while it appeared in the blend without copolymer at a weight ratio of 20/80. DMA results showed that by adding the copolymer, both the glass transition temperature (T_g) of the PI component and the α-relaxation of HDPE shifted to lower temperature, demonstrating the enhanced penetration of the two components. Mechanical properties of the blends were improved, especially the elongation at break, by the presence of the copolymers. The characteristic yielding at the fractured surface of the blends compatibilized with the copolymer indicates the fractural behavior of the material changed from brittle to tough.