Mécanismes de déformation et comportement mécanique d'alliages de titane β du Ti20V au Ti20V6Al. Résultats expérimentaux et modélisation

摘要

In the present work we have studied alloys of β-titanium (in all cases these were single phase prior to plastic deformation) having compositions Ti20VXAl where X was varied in the range 0 to 6 %. The alloys containing up to 4 % aluminium deform principally by {332} < 113 > twinning associated with a phase transformation to the phase ω_s. Crystallographic slip intervenes later, preferentially on planes of the type {110}. Alloys containing 5 % or more aluminium deform principally by Crystallographic slip. The choice of active deformation modes is confirmed by the good prediction of the cold rolling texture. Correlations between the deformation processes and the mechanical properties confirm that there is a sound basis for optimizing the mechanical behaviour of these alloys.%Cette étude concerne des alliages de titane β (exclusivement monophasé avant la déformation plastique) de composition Ti20VXAl avec X variant de 0 à 6 %. Les alliages qui contiennent jusqu'à 4 % d'aluminium se déforment essentiellement par maclage de type {332}< 113 > associé à une transformation de phase ω_s. Le glissement cristallographique intervient ensuite, préférentiellement sur les plans de type {110}. Les alliages qui contiennent 5% et plus d'aluminium se déforment essentiellement par glissement cristallographique. La modélisation de l'évolution de texture lors d'un laminage à froid a permis de confirmer la sélection des mécanismes activés et de les expliquer. Les corrélations entre mécanismes de déformation et propriétés mécaniques confirment qu'il est possible d'optimiser le comportement mécanique de ces alliages.