Large electrostrictive actuation of barium titanate single crystals

摘要

An experimental investigation of the electromechanical behavior of single crystals of the ferroelectric perovskite barium titanate is presented. An experimental setup has been designed to investigate large strain actuation in single crystal ferroelectrics subjected to combined electrical and mechanical loading. Experiments have been performed on initially single domain crystals of barium titanate with (100) and (001) orientation at compressive stresses between 0 and 5 MPa. Global strain and polarization histories have been recorded. The electrostrictive response is shown to be highly dependent on the level of applied stress with a maximum strain of 0.9% measured at a compressive stress of about 2 MPa and electric field of about 10 kV/cm. This level of strain is about 5 times higher than in typical commercial piezoelectric PZT. Polarized light microscopy has been used to observe the evolution of the domain pattern simultaneously with the strain and polarization measurement. The observations reveal that the observed large strain behavior is the result of 90°domain switching.