On the nonlocal nature of dislocation nucleation during nanoindentation

摘要

Using static atomistic simulations, we study the full details of the mechanism by which dislocations homogeneously nucleate beneath the surface of a initially defect-free crystal during indentation. The mechanism involves the collective motion of a finite