レーザー加熱延伸したPVDFモノフィラメントの構造と力学的性質

摘要

The poly(vinylidene fluoride) monofilaments having diameter of 0.2 - 0.7 mm were drawn with heating by laser irradiation. It is estimated that the filament which have a diameter of 0.2 mm can be heated almost uniformly by the laser irradiation whereas only outer layer of the filament of 0.7 mm can be heated. Therefore, the 0.7 mm filament cannot be drawn stably under low drawing stress. And for the higher draw ratio, the drawing stress concentrated to the central part of the filament. The cross-sectional stress deviation in the filament with diameter of 0.7mm causes the a-form crystal remaining up to higher drawing stress, and restraining tensile strength of drawn filaments. By redrawing of the drawn filament still remaining a-form crystal not only improves the attaining tensile strength but also reduces the thermal shrinkage of drawn filaments.%ポリフツ化ビニT）デン（Poly（vinylidene fluoride），以下PVDF）はフッ素系のエンジニアリングプラスチックであり，焦電性，圧電性，強誘電性等の電気的性質を生かした有機電子材料［1］分野や，高い強度，耐薬品性の高さ，良好な成形加工性を生かした膜材料［2］として利用されている．またPVDFモノフィラメントは，吸水性がほとんどなく，屈折率が水に近い，比重が大きい，耐光性に優れているという性質を持っているため，魚網や釣り糸などの漁業用資材として使用されており［3］，マグロ延縄用のテグスなどでは直径が3mmを超える太いフィラメントも使用されている．