A novel method to investigate tensile properties of woven fabrics in all-direction

摘要

In this research, we propose a new method and instrument to measure load-extension curve of the fabric samples under all-directional extension. Using this method, fabric sample is loaded under extension in the warp, weft, and all other directions in between. Using this new method, we introduced a comprehensive tensile modulus which is affected by the fabric structures and densities. For this purpose different structures i.e. plain, Twill 2/2, Twill 1/3, and Twill 1/7 were produced with different densities. Then these samples were tested under the new method. Our results are then compared to those one would obtain under uniaxial tests, by performing independent uniaxial tests. It is shown that under all-directional test lowering the weft density decreases the tensile comprehensive modulus. Furthermore, a reduction in the floating yarns in the fabric structure decreases the tensile comprehensive modulus. It was found that among the samples tested here, plain fabric and Twill 1/7, respectively, possess the maximum and minimum comprehensive modulus. A similar trend was also observed through independent uniaxial extension, in warp or weft direction, test.