Preparation and properties of functionalized multiwalled carbon nanotubes/polypropylene nanocomposite bipolar plates for polymer electrolyte membrane fuel cells

摘要

Multiwalled carbon nanotubes (MWCNTs) are covalently modified with different molecular weights 400 and 2000 poly(oxyalkylene)-amine bearing the diglycidyl ether of bisphenol A (DGEBA) epoxy (POA400-DGEBA and POA2000-DGEBA) oligomers. The oxidized MWCNTs (MWCNTs-COOH) are converted to the acid chloride-functionalized MWCNTs, followed by the reaction with POA-DGEBAs to prepare the MWCNTs/POA400-DGEBA and MWCNTs/POA2000-DGEBA FT1R, thermogravimetric analysis (TGA) and high resolution X-ray photoelectron spectra (XPS) reveal that the POA-DGEBAs are covalently attached to the surface of MWCNTs. The morphology of MWCNTs/POA-DGEBA is observed by TEM. The POA400-DGEBA coated on the MWCNTs is thicker and more uniform. However, the coating of POA2000-DGEBA on the MWCNTs shows a worm-like bulk substance and the MWCNT surface is bare. In addition, the flexural strength and the bulk electrical conductivity of the MWCNTs/polypropylene nanocomposite bipolar plates are measured 59% and 505% higher than those of the original composite bipolar plates by adding 8 phr of MWCNTs/POA400-DGEBA. The maximum current density and power density of the single cell test for the nanocomposite bipolar plate with 4 phr MWCNTs/POA400-DGEBA are 1.32 A cm~(-2) and 0.533 W cm~(-2), respectively. The overall performance confirms the functionalized MWCNTs/polypropylene nanocomposite bipolar plates prepared in this study are suitable for PEMFC application.